AISI H10 /din 1.2365 32CrMoV12-28 h10 jis skd7 steel bar
1.2365 steel bohler
TOOL STEEL FOR HOT WORKING 32CRMOV12-28, 1.2365, AISI H-10 ACCORDING TO ISO 4957.
| Standard | Steel Grade | ||||||||
|---|---|---|---|---|---|---|---|---|---|
| Chemical Composition % | |||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | V: | ||
| ISO | 1.2365 - 32CrMoV12-28 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.02 | 2.7 - 3.2 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| DIN | 32CrMoV3-3 - 32 CrMoV 3-3 | ||||||||
| 0.28 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.7 - 3.2 | 2.6 - 3.0 | 0.4 - 0.7 | ||
| PN | WLV | ||||||||
| 0.25 - 0.35 | 0.25 - 0.50 | 0.15 - 0.40 | <0.03 | <0.03 | 2.5 - 3.0 | 2.5 - 3.0 | 0.4 - 0.6 | ||
| EN | 30CrMoV12-11 | ||||||||
| 0.25 - 0.35 | 0.15 - 0.45 | 0.1 - 0.4 | <0.03 | <0.03 | 2.5 - 3.5 | 2.5 - 3.0 | 0.4 - 0.7 | ||
| ASTM | AISI H-10 - UNS T20810 | ||||||||
| 0.35 - 0.45 | 0.2 - 0.7 | 0.8 - 1.25 | <0.03 | <0.03 | 3.00 - 3.75 | 2.0 - 3.0 | 0.25 - 0.75 | ||
| GOST | 3H3M3F - | ||||||||
| 0.27 - 0.34 | 0.2 - 0.5 | 0.1 - 0.4 | <0.03 | <0.03 | 2.8 - 3.5 | 2.5 - 3.0 | 0.4 - 0.6 | ||
1.2365, 32CrMoV12-28, X32CrMoV3-3 - specifications and applications
Tool steel for hot working, used for production of press matrices, die inserts, moulds for casting non-ferrous metals, tools and stamps for pressing and stamping. It is characterized by high hardenability, excellent thermal conductivity, resistance to temperature differences during water cooling, and tempering resistance. It achieves hardness levels of 52 HRC.
Mechanical properties of 1.2365, 32CrMoV12-28 steel
Hardness in +A delivery condition: <229 HB Hardness in +A+C delivery condition: <249 HB Hardness after hardening: 52 HRC Hardness after hardening and tempering at temperature: 300℃ = 47.2 HRC 350℃ = 47.6 HRC 400℃ = 48.5 HRC 450℃ = 50.0 HRC 500℃ = 51.7 HRC 550℃ = 51.9 HRC 600℃ = 49.0 HRC Thermal conductivity, λ: 36 W * m-1 * K-1 Linear expansion coefficient, α: 12.4 * 10-6 K-1
Heat treatment of 1.2365, 32CrMoV12-28 steel
Softening annealing at 740 - 770℃ Relief annealing at 600 - 700℃ Hardening at 1030 - 1050℃ Tempering at 450 - 550℃ Nitriding at 470 - 550℃
2.Product Application Areas:
Our products have been used in all kinds of areas, such as aviation,aerospace,navigation,nuclear energy,chemical industry,
electronic information,achine manufacture, petrochemical, automotive,instrument and meter, Communication ,transportation, and medical instruments, etc.
3.Similar steel grade & equivalent steel materials:
|
USA |
Japanese |
Gemany |
British |
France |
heat treatment |
Chinese |
|
ASTM&AISI&SAE |
JIS |
EN DIN |
EN BS |
EN NF |
ISO |
GB |
|
AISI H10 |
1.2365 |
------ |
||||
1.2365 steel bohler and bar from factory
Popularni tagovi: 1.2365 steel bohler jis skd7, China, manufacturers, suppliers, factory